Linya sa Produksyon sa Carbon Fiber Precursor
Deskripsyon
Ang carbon fiber precursor production method nga nagsagop sa Dimethyl Sulfoxide(DMSO) isip solvent, Acrylonitrile(AN) isip unang monomer, Itaconic Acid isip ikaduhang monomer, AIBN isip initiator nga adunay binary copolymerization, ug ang dry-jet wet spinning mao ang nag-unang pagpili nga giuyonan sa mga eksperto sa carbon fiber.
Tech Specs:
Dili. | butang | Yunit | Mga detalye | Mga komento |
1 | Linear Densidad | dtex | 1.15 | |
2 | Kusog sa tensile | CN/dtex | ≥4.0 | |
3 | Elongation | % | 12±2 | |
4 | Dimethyl Sulfoxide(DMSO) Content | % | <0.03 | |
5 | Langis nga sulod | % | 0.5-0.1 | |
6 | Katapusan nga Rate sa Pagkaguba | % | <3 | |
7 | Umog Pag-usab | % | ≤1 | |
8 | Panagway | Walay Dayag nga Naputol nga Filament |
Proseso:
Pagpangandam sa Hilaw nga Materyal —→ Monomer Mixture —→ Copolymerization —→ Primary Filtration —→ Monomer Removal —→ Secondary Filtration —→ Mixed Batch Neutralization —→ Tertiary Filtration —→ Storage —→ Defoam —→ Spinning —→ spin bath (Primary) —→ spin bath bath (Secondary) —→ spin bath (Tertiary) —→ Limpyo —→ Hot Stretching —→ Oiling —→ Pagpauga —→ Steam Stretching —→ Heat Setting —→ Antistatic Treatment —→ Precursor Winding
Dili. | butang | Yunit | Mga detalye | Mga komento |
1 | Linear Densidad | dtex | 1.15 | |
2 | Kusog sa tensile | CN/dtex | ≥4.0 | |
3 | Elongation | % | 12±2 | |
4 | Dimethyl Sulfoxide(DMSO) Content | % | <0.03 | |
5 | Langis nga sulod | % | 0.5-0.1 | |
6 | Katapusan nga Rate sa Pagkaguba | % | <3 | |
7 | Umog Pag-usab | % | ≤1 | |
8 | Panagway | Walay Dayag nga Naputol nga Filament |
Raw Pag-andam sa Materyal —→ Monomer Mixture —→ Copolymerization —→ Primary Filtration —→ Monomer Removal —→ Secondary Filtration —→ Mixed Batch Neutralization —→ Tertiary Filtration —→ Storage —→ Defoam —→ Spinning —→ spin bath (Primary) —→ spin bath bath (Secondary) —→ spin bath (Tertiary) —→ Limpyo —→ Hot Stretching —→ Oiling —→ Pagpauga —→ Steam Stretching —→ Heat Setting —→ Antistatic Treatment —→ Precursor Winding